Thin Super Glue 20 g

Product detailed description

Thin Super Glue 20 g

High-quality thin cyanoacrylate super glue with high strength for workshop and general use. Supplied in a bottle with a clog-resistant applicator nozzle. The adhesive forms a strong bond within 1–5 seconds.

The very low-viscosity thin super glue is ideal for bonding non-porous and porous materials that fit perfectly together – a typical application is gluing RC car tires to rims. Bonds wood, most plastics, metals, rubber, glass, ceramics, cork, and paper. Apply the adhesive to precisely aligned parts that are already positioned together.

Properties

• color: clear

• viscosity: 12–22 mPa·s

• density: 1.04–1.06 g/cm³

• optimal application temperature: 25 °C

• curing time (depends on temperature and materials):

  • nitrile rubber < 5 s

  • stainless steel 15–20 s

• full cure: 24 h

• shear strength: 15–25 N/mm²

• operating temperature range: −10 °C to +40 °C

• maximum temperature range: −40 °C to +85 °C

• optimal gap between bonded parts: zero

• cured adhesive is soluble in acetone, dimethylformamide, and acetonitrile

Additional information and recommendations

• If the super glue thickens, it indicates partial polymerization and loss of original properties. These cannot be restored by “thinning”.

• If you need a thinner adhesive, simply use a type with lower viscosity.

• Different KAVAN PRO super glues can be mixed to achieve optimal viscosity.

• When using the glue as a filler, we recommend the KAV9980 CA microballoon filler.

• Suitable for bonding soft and hard wood, chipboard, plywood, metals, ceramics, porcelain, glass and carbon laminates, glass and carbon fabrics and fibers, and many plastics (including EPP and EPO).

• Not suitable for bonding polystyrene foam, polyethylene, Teflon, or silicone.

• Store tightly closed in a cool, dry, dark place (+2 °C to +10 °C). Do not expose to temperatures below +2 °C.

• When stored correctly, shelf life in unopened original packaging is 1 year while maintaining the above properties.